【摘要】 采用商品化的PtRu/C和Pt/C分别作乙醇阳电极和氧气阴电极的催化剂 ,Nafion 115膜作固体电解质 ,组装成面积为 9cm2 的单池 .考察了电池温度、氧气压力、乙醇浓度及流量等对电池性能的影响 .实验结果表明在电池温度为 85℃ ,乙醇浓度为 1.0mol/L ,流量为 0 .5mL/min ,氧气压力为 0 .5MPa ,流量为 6 8mL/min条件下 ,电池开路电压为 0 .6 0 8V ,电流密度 5 0mA/cm2 时的放电端电压为 0 .32 9V ,电池最大功率密度为 19.2 5mW /cm2更多还原

【Abstract】 The performance of a direct ethanol fuel cell based on Nafion115 was reported.PtRu/C and Pt/C were used as ethanol anode and oxygen cathode catalysts in a single cell of size 9 cm 2 .The effects of temperature,oxygen pressure,the flow rate of ethanol, and oxygen, and ethanol concentration were tentatively studied.The experimental results showed that the cell open circuit voltage 0.608 V,the cell voltage 0.329 V at 50 mA/cm 2 ,and the peak power density 19.25 mW/cm 2 were reached under the conditions of T cell =85 ℃, P O2 =0.5 MPa, C ethanol =1.0 mol/L and with the flow rate of ethanol and oxygen being 0.5 mL/min and 68 mL/min separately.更多还原