铁基自熔合金光束熔覆层的微观组织及强化机理

Microstructure and Strengthening Mechanism of Light Beam Cladding Layer with Iron-based Self-fluxing Alloy Powder

  • 推荐 CAJ下载
  • PDF下载
  • 不支持迅雷等下载工具,请取消加速工具后下载。

【作者】 单际国丁建春任家烈

【Author】 SHAN Ji guo (Department of Mechanical Engineering,Tsinghua University,Beijing 100084,China),DING Jian chun,REN Jia lie.

【机构】 清华大学机械工程系!北京100084

【摘要】 采用SEM、EDS、X射线衍射及显微硬度和洛氏硬度分析手段研究了铁基自熔合金粉末光束熔覆层的微观组织及其物相组成。结果表明 ,Fe Ni Cr B Si系合金粉末的光束熔覆层微观组织由固溶了大量Cr、及少量B、Si、C的γ(Fe,Ni)树枝晶 ,枝晶间(Cr,Fe) 7(C ,B) 3+γ(Fe,Ni)共晶所构成。光束熔覆层的宏观硬度达HRC4 7.3 ,高于同种材料喷涂层及TIG熔覆层的硬度。Cr、Si元素在γ相中的固溶 ,枝晶间共晶 (Cr,Fe) 7(C ,B) 3高硬度相的析出是光束熔覆层得以强化的主要原因。

【Abstract】 Microstructure and phase structure of light beam cladding layer with iron based self fluxing alloy powder were studied by SEM,EDS,X ray diffraction,microhardness and Rockwell hardness.The results showed that the microstructure of Fe Ni Cr Si B alloy powder light beam cladding layer was composed of γ (Fe,Ni) dendrite which dissolved a lot of Cr and little B,Si,C ,and (Cr,Fe) 7 (C,B) 3 + γ (Fe,Ni) eutectic among dendrite.The macrohardness of the light beam cladding layer reached HRC47.3,which was higher than that of spraying layer and TIG cladding layer with the same powder.The main reason of strengthening of the light beam cladding layer was the solution of Cr,Si elements in γ phase and the precipitation of high hardness (Cr,Fe) 7 (C,B) 3 .

【基金】 国家自然科学基金 ( 5 990 5 0 17);国家机械行业“九五”攻关项目 (JHG -15 ) ;清华大学 985基础研究基金;清华大学实验室开放基金
  • 【文献出处】 焊接学报 ,Transactions of The China Welding Institution , 编辑部邮箱 ,2001年04期
  • 【分类号】TG174.44
  • 【被引频次】45
  • 【下载频次】248
节点文献中: 

本文链接的文献网络图示:

本文的引文网络