节点文献
Sr1-xBixFeO3-δ（x≤0.50）的柠檬酸盐法制备和导电性
Preparation and Conductivity of Sr1-xBixFeO3-δ（x≤0.5） by Citrate Methods
【摘要】 采用柠檬酸盐法制备了Sr1－xBixFeO3－δ（x≤0.50）系列氧离子-电子混合导体，并采用XRD、IR、TG、DTA和交流复阻抗技术对产物进行了表征．初始凝胶经自燃和800℃下预烧，可得纯相钙钛矿产物粉体，其结构与SrFeO3相似，为正交对称性．粉体在850～900℃下烧结，可得相对烧结密度在97％以上的烧结体．Sr0.5Bi0.5FeO3－δ的电导率在400℃出现极值，约为3．6Scm－1．
【Abstract】 Sr1-xBixFeO3-δ (x≤0.50) series oxide ionic/electronic conductors were prepared through citrate gel precursors. The product was characterized by means of XRD, IR, TG, DTA and ac impedance techniques. Pure perovskite-type phase was formed after the gel combusted and calcined at 800℃, and had an orthorhombic structure similar to that of SrFeO3. Although the density of the product calcined at 85O"C remained 97% theoretical value, an extreme conductivity of 3.6Scm-1 was found at 400℃.
【关键词】 氧离子-电子混合导体；
柠檬酸盐法；
钙钛矿；
Sr1－xBixFeO3-δ（x≤0.50）；
【Key words】 oxide ionic/electronic conductor； citrate gel method； perovskite； Sr1-xBixFeO3-δ（x≤0.50）；
【Key words】 oxide ionic/electronic conductor； citrate gel method； perovskite； Sr1-xBixFeO3-δ（x≤0.50）；