【Abstract】 Hydration behavior and related physical properties of cement at lower temperatures (2～8℃) with natural gypsum replaced by calcined gypsum and calcined alunite were studied,and XRD,DTA and SEM measurement analyses were conducted.Experimental results show that,when calcined gypsum and calcined alunite were added by 5% alone or synchronously,the setting time of cement decreases remarkably and 3d compressive strength at different temperatures increases remarkably.The increase of 3d compressive strength is attributed to the increase of AFt and the decrease of Ca(OH) 2 in hardened cement paste.更多还原