重压下技术在34CrMo4气瓶钢上的应用研究
Study on Application of Heavy-reduction technology in 34CrMo4 Gas Bottle Steel
【Author】 Li-Jianquan;Li-Yangzhou;Wu Guorong;Ji-Cheng;Lei-Yangwei;PanGang Group steel & Vanadium Co.,Ltd.;PanGang Group Research Institute Co.,Ltd.;School Metallurgy, Northeastern University;
【机构】 攀枝花钢钒有限公司提钒炼钢厂； 攀钢集团研究院有限公司； 东北大学冶金学院；
【摘要】 针对某公司360mm×450mm断面生产CrMo系气瓶钢存在的中心疏松、缩孔问题,结合大方坯连铸机改造,新增凝固末端重压下装备技术后,开展了重压下工艺的现场探索试验。试验表明:压下量增大有利于减小铸坯中心疏松带宽度,有利于改善连铸坯内部质量。
【Abstract】 In view of the problem of central porosity and shrinkage in the production of CrMo gas bottle Steel in 360 mm×450 mm section of a company, the field exploration test of the technology under heavy pressure was carried out after the renovation of bloom continuous caster and the new Heavy Reduction equipment technology of solidification end. The results show that the increase in pressure decreases the width of the center porosity and improves the internal quality of continuous casting bloom.
【Key words】 Bloom； steel for gas bottle； Heavy Reduction； central porosity；