燃煤电厂低温蜂窝状Mn-Ce/TiO2 SCR催化剂的实验研究
【机构】 新疆国泰新华矿业股份有限公司； 浙江天蓝环保技术股份有限公司； 浙江大学环境工程研究所； 浙江省能源研究会；
【摘要】 本文重点考察催化剂制备工艺以及不同添加剂对催化剂强度和抗水性能的影响。通过改进制备工艺参数及配方优化,催化剂轴向强度和径向强度分别达到4.9MPa和1.1MPa,超过现有商业SCR催化剂。活性测试表明,现有催化剂在120℃时的NO转化率最高达到97.53%,引入8%的水汽稳定后,NO转化率仍高达81%左右,具有较高的低温活性和抗水性。
【Abstract】 This manuscript mainly studied the affection of the catalyst preparation process and different additives on catalyst strength and water-resistance.Through the improvement of preparation process and the optimization of the catalyst formula,the lengthwise and crosswise strength of the catalyst exceed 4.9 MP and 1.1 MPa,respectively,which were all higher than the commercial catalyst.Furthermore,97.53%NO conversion was achieved at the temperature of 120 ℃ in the activity tests.After intruding 8%water vapor,the NO conversion also maintained around 81%,which showed high low temperature activity and fine water-resistance.
【Key words】 low temperature SCR catalyst； Mn； Ce； Strength； Water-resistance；
- 【会议录名称】 推进雾霾源头治理与洁净能源技术创新——第十一届长三角能源论坛论文集
- 【会议名称】2014年第十一届长三角能源论坛
- 【会议时间】2014-11-25
- 【会议地点】中国上海
- 【分类号】TQ426;TM621
- 【主办单位】中国工程院能源与矿业工程学部、上海市中国工程院院士咨询与学术活动中心、上海市能源研究会