【作者】 张平则； 缪强； 姚正军； 黄俊； 吴红燕； 周朴； 严锦山； 冯立新；

【Author】 ZHANG Pingze~1 MIAO Qiang YAO Zhengjun~1 HUANG Jun~1 WU Hongyan~1 ZHOU Pu~1 YAN Jingshan~2 FENG Lixin~2 1. Nanjing University of Aeronautics and Astronautics, Nanjing 210016 2. Wuxi Linlong Aluminium Co. LTD, Wuxi 214183

【机构】 南京航空航天大学材料科学与技术学院； 无锡麟龙铝业有限公司；

【摘要】 本文研究了热镀 Al-Zn-Si-RE-Mg 涂层的耐蚀耐磨性能,并将其与热镀锌涂层、热镀 Al-Zn-Si 涂层、热镀 Al-Zn-Si-RE 涂层对比。结果表明热镀 Al-Zn-Si-RE-Mg 涂层的耐磨性最好,磨损量只有热镀锌涂层的1/14。更多还原

【Abstract】 Wear resistance of hot-dip Al-Zn-Si-RE-Mg coating were investigated,compared with hot-dip zinc coating,hot-dip Al-Zn-Si coating and hot-clip Al-Zn-Si-RE coating.By pin-on-disc tribometer.The results of wear tests showed that the wear resistance of hot-dip Al-Zn-Si-RE-Mg coating was best of all,and its wear lost was only one fourteenth of the hot-dip zinc coating’s.更多还原