热塑性变形条件下钢内部裂纹愈合的实验研究

EXPERIMENTAL STUDY ON INNER CRACK HEALING IN STEEL DURING HOT PLASTIC DEFORMING

  • 推荐 CAJ下载
  • PDF下载
  • 不支持迅雷等下载工具,请取消加速工具后下载。

【作者】 韦东滨韩静涛谢建新付晨光王连忠贺毓辛

【Author】 WEI Dongbin HAN Jingtao XIE Jianxin FU Chenguang WANG Lianzhong HE Yuxin School of Materials Science and Engineering,University of Science and Technology Beijing,Beijing 100083

【机构】 北京科技大学材料科学与工程学院

【摘要】 在HIGH-MULTI 5000型热压机上对含有人工预置内部裂纹的20MnMo钢及20号钢试样进行了愈合实验.发现热塑性变形条件下,存在于预置内部裂纹区域的裂纹缝隙消失,裂纹完全愈合,愈合区内为铁素体,与无塑性变形、仅经过高温处理的试样内部裂纹形态进行对比,表明热塑性变形条件下愈合进程大大加快,但愈合区与基体组织形态不一致的状况并未改善.

【Abstract】 The test that tries to heal inner crack in 20MnMo steel and 20 steel was carried out by using HIGH-MULTI 5000 hot-press cquipment.Under the hot plastic deforming,the inner crack can be healed completely and ferrite has been discovered in the healing area.Contrasting to the results of high temperature hesling treatment without plastic deforming,the healing process with hot plastic deforming is developed rapidly.Structural inhomogeneity between healing area and matrix can not be improved.

【关键词】 内部裂纹愈合
【Key words】 steelinner crackhealing
【基金】 国家自然科学基金重点资助项目59889101;国家自然科学基金资助项目59771068
  • 【会议录名称】 2007轧钢与锻造过程中的裂纹控制技术学术研讨会论文集
  • 【会议名称】2007轧钢与锻造过程中的裂纹控制技术学术研讨会
  • 【会议时间】2007-08
  • 【会议地点】中国北京
  • 【分类号】TG142.15
  • 【主办单位】中国金属学会青年委员会、北京机械工程学会
节点文献中: 

本文链接的文献网络图示:

本文的引文网络