Ca0.5Sr0.5CoxFe1-xO3-δ对CO2的吸附性及反应性研究
Adsorption and Reactivity of Ca0.5Sr0.5CoxFe1-xO3-δ to Carbon Dioxides
【Author】 ChenChaoqun, Zhang Mei, Yan Baijun, Feng Gensheng, Li Liansheng (School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, China)
【机构】 北京科技大学冶金与生态学院；
【摘要】 利用固相合成法在1100和1200℃下合成了钙铁矿材料Ca0.5Sr0.5CoxFe1-xO3-δ,在CO2气氛下的对其进行了TG-DSC综合热分析, 结果表明材料对CO2具有一定的吸附性能,在800℃左右出现吸附量最大值。材料用于CO2催化分解的实验结果显示,在800℃时材料对CO2具有很好的催化分解能力。通过对用后的Ca0.5Sr0.5CoxFe1-xO3-δ的XRD物相分析,证明材料中的碱土金属离子与CO2发生了反应。
【Abstract】 Brownmillerites of Ca0.5Sr0.5CoxFe1-xO3-δ were synthesized by using solid reaction method at 1100 and 1200 ℃, respectively. The experimental results of TG-DSC of Ca0.5Sr0.5CoxFe1-xO3-δ under CO2 atmosphere show that these materials can adsorb carbon dioxide to certain extent, with a maximum adsorption at about 800 ℃. The result of pyrolysis of CO2 show that the materials can decompose CO2 catalytically at 800℃. The XRD characterization of Ca0.5Sr0.5Co0.7Fe0.3O3-δdemonstrates that the alkaline earth ions in the materials react with CO2.
【Key words】 brownmillerite； TG-DSC； carbon dioxide； adsorption； catalytical pyrolysis of carbon dioxide；