【作者】 刘春； 邹华维； 徐闻； 刘鹏波；

【Author】 LIU Chun ZOU Huawei XU Wen LLU Penbo (The State Key Lab. of Polymer Materials Engineering, Polymer Research Institute of Sichuan University, Chengdu 610065,China)

【机构】 高分子材料工程国家重点实验室四川大学高分子研究所；

【摘要】 <正>聚氯乙烯(PVC)在机械稳定性、耐化学药品性和阻燃性等方面具有优异的性能,但由于其抗冲击性、热稳定性及加工性能方面的不足,使其应用受到了很大限制。为进一步拓展其应用领域,目前开发了多种抗冲击改性剂,如乙烯-醋酸乙烯共聚物(EVA)、氯化聚氯乙烯 (CPE)、丙烯酸酯(ACR)、甲基丙烯酸甲酯-丁二烯-苯乙烯共聚物(MBS)等,其中采用MBS 增韧的同时能较好的保持PVC的透明性。苯乙烯-丁二烯-苯乙烯嵌段共聚物(SBS)具有更多还原

【Abstract】 The properties of transparent PVC/SBS blend compatibilized with MBS was studied through spectrophotometer, Optical microscope, SEM and impact strength testing. The experimental results show that with the addition of MBS in PVC/SBS blend, the interfacial interaction between PVC and SBS was improved, the impact strength was thus increased. The vitrification rate of PVC/SBS /MBS blend (PVC/modifiers: 92/8) reaches a maximum value when MBS/SBS is 20/80.更多还原