Al2O3/Al复合涂层对贫铀的保护性能研究
Protection of Al2O3/Al Multi-layer Coatings for Depleted Uranium
【Author】 LU Xuechao Wang Xiaolin Lang Dingmu Zhang Yanzhi(China Academy of Engineering Physics, Mianyang 621900, china)
【机构】 中国工程物理研究院；
【摘要】 采用盐雾腐蚀和磨损试验考核,结合SEM/EDS和XRD表征,分析了贫铀表面Al2O3/Al复合涂层的保护性能。结果表明,贫铀表面反应磁控溅射Al2O3/Al涂层没有明显的腐蚀特征,而等离子喷涂Al2O3/Al涂层发生了严重的腐蚀剥落现象。Al2O3/Al涂层表现为磨粒磨损行为,抗磨损性好。作为对比样的贫铀表面Al涂层则表现为粘着磨损行为,抗磨损性差。讨论了贫铀表面涂层的腐蚀和磨损行为。
【Abstract】 Protection of Al2O3/Al multi-layer coatings for depleted uranium was investigated by using a combination of 5%NaCI salt fog and abrasion test with SEM/EDS and XRD profiles. The results indicate that Reactive Magnetron Sputtered Al2O3/Al coatings appear no obvious corrosion compared to the serious spallation of Plasma Sprayed Al2O3/Al coatings. The Al2O3/Al coatings are wear-resistant much better than the Al. The corrosion and abrasion behaviors of all coatings are discussed.
【Key words】 uranium； magnetron sputtering； Al2O3/Al coatings； protection；
- 【会议录名称】 2004全国荷电粒子源、粒子束学术会议论文集
- 【会议名称】2004全国荷电粒子源、粒子束学术会议
- 【会议时间】2004-08
- 【会议地点】中国乌鲁木齐
- 【分类号】TL214
- 【主办单位】中国电工技术学会电子束离子束专业委员会、粒子加速器学会离子源专业组、中国电子学会焊接专业委员会、北京电机工程学会加速器专业委员会