二氧化锰涂覆EPS方法与效能分析
Research on the methods and properties of coating EPS MnO2 absorbing spheres
【Author】 YANG Wei-wei LIU Shun-hua DU Ji-zhu (Material Engineering Department,Dalian University of Technology,Dalian 116023,China)
【机构】 大连理工大学材料科学与工程学院；
【摘要】 采用直接涂覆法将二氧化锰涂覆在 EPS 表面制成吸波球体．实验证实,这种方法有能力涂覆大密度导电粉末,且效果良好,在反射阻抗的测试中,当试样厚度为10mm 时,其反射损耗在8～18GHz 频率范围内为 -7～-15dB,发现随着吸波颗粒中二氧化锰含量和试样厚度的增加,在8～18GHz 频段内,试样的反射损耗增加．二氧化锰层吸波球体效能略低于同等导电层厚度的炭粉层吸波球体．
【Abstract】 MnO2 was coated on the EPS-based absorbing spheres by fluid coating in this work.The results demonstrate this method to be efficient in coating dense conductive powder.The proof sample with a thickness of 10mm have an absorbing property of -7--15dB in the frequency 8-18GHz.Moreover,the absorbing property increases with the increasing MnO2 content in the absorber within the same frequency range.The absorbing property of the spheres covered by MnO2 is lower than that covered by carbon black with the same thickness of the conductive layer.
- 【会议录名称】 第六届中国功能材料及其应用学术会议论文集（8）
- 【会议名称】第六届中国功能材料及其应用学术会议
- 【会议时间】2007-11
- 【会议地点】中国湖北武汉
- 【分类号】TB34
- 【主办单位】重庆仪器材料研究所、中国仪器仪表学会仪表材料分会、国家仪表功能材料工程技术研究中心