Tb0．5Dy0．5(Fe1-xMnx)1．91（x=0～0．15）合金的温度性能研究
Study on temperature properties of Tb0.5Dy0.5(Fe1-xMnx)1.91（x=0～O.15）alloys
【Author】 HONG Xing ZHANG Hong-ping ZHAO Dong-liang (Research Institute of Functional Materials,Central Iron & Steel Research Institute,Beijing 100081,China)
【机构】 钢铁研究总院功能材料研究所；
【摘要】 研究了 Mn 元素掺杂及热处理工艺对超磁致伸缩材料 Tb0.5Dy0．5(Fe1-xMnx)1．91（x=0～0．15）合金温度性能的影响,实验结果表明 Mn 掺杂对该材料居里温度影响较大,随 Mn 掺杂量的增加居里温度降低；在无预压应力时,Mn 掺杂提高了合金的低温、低场磁致伸缩应变性能；热处理工艺对进一步提高磁致伸缩性能无明显作用。
【Abstract】 Magnetostriction temperature dependencies of Tb0.5Dy0.5(Fe1-xMnx)1.91（x=0-0.15）alloys and heat-treating effects is presented.The results showed that Mn substitution influence on the Curie temperature observably,and the Curie temperature decrease when Mn content increase.The substituting Mn for Fe is effective to improve their magnetostrictive property at cryogenic temperature and low magnetic field under no pre-stress.On the other hand,heat-treatment is useless to improve magnetostrictive property in this experimentation.
【Key words】 Tb0.5Dy0.5(Fe1-xMnx)1.91 alloys； substitution； heat-treated； magnetostrictive property； Curie temperature；