一种光致荧光材料的制备方法及其光谱特性研究
Study on preparation method and spectrum properties of SrS:Eu,Sm
【作者】 陈朝阳； 刘艳平； 范艳伟； 巴维真； 杜彦召； 王军华；
【Author】 CHEN Zhao-yang LIU Yan-ping FAN Yan-wei BA Wei-zhen DU Yan-zhao WANG Jun-hua (Xinjiang Technical Institute of Physics & Chemistry,Chinese Academy of Sciences,Urumqi 830011,China)
【机构】 中国科学院新疆理化技术研究所；
【摘要】 采用碳还原法合成 SrS：Eu,Sm,研究了灼烧温度及灼烧时间对样品发光性能的影响．通过 X 射线衍射(XRD)测试证明合成材料纯度较高,样品具有 SrS 的面心立方结构,晶格常数为0．601nm。样品的激发谱峰值在272、340、466nm 处,荧光光谱的峰值在 614nm 处,光激励发光峰为608nm,光激励发光的光谱响应范围为800～1400nm。
【Abstract】 SrS:Eu,Sm was prepared by carbon reduction method.The effect of calcination temperature and time on luminescence intensity were studied.XRD patterns indicated that the synthetically materials have single phase and the samples prepared were with face-center cubic structure and the lattice parameter was 0.601nm.Excitation spectrum peaking of sample was at 272,340 and 466nm.The peaking of fluorescence spectrum was at 603nm.The photo-stimulation luminescence spectrum peaking was at 608nm.The wavelength response range of the photo-stimulation luminescence is located at 800-1400nm.
【Key words】 carbon reduction method； electron trapping； photo-stimulated luminescence；