不同成型工艺对纳米碳管电极电吸附脱盐性能的影响
Study on the electric adsorption-desalination of carbon nanotube electrodes with different moulding
【Author】 ZHANG Deng-song, DAI Kai, FANG Jian-hui, CAO Wei-min, SHI Li-yi (School of Science, Shanghai University, Shanghai 200436, China)
【机构】 上海大学理学院；
【摘要】 分别采用酚醛树脂(PR)为粘结剂热压和聚四氟乙烯(PTFE)为粘结剂冷压的成型工艺制备电吸附脱盐器的纳米碳管(CNTs)电极,利用氮气吸附分析电极表面结构,结果表明热压成型电极比表面积较大,所形成的孔隙基本为中孔,平均孔径大于盐水中水合Na+和Cl-的有效半径;结合扫描电镜(SEM)和水珠接触角测试分析,发现热压成型电极表面空隙丰富,亲水性强;进行充放电测试,发现热压成型电板电吸附性能显著优于冷压成型电极,故热压成型纳米碳管电极脱盐性能优越。
【Abstract】 The carbon nanotube electrodes are moulded with different methods. One is hot-moulded with phenolic resin (PR) binder; the other is moulded with polytetrafluoroethylene (PTFE) binder. The surfacial structure of carbon nanotube electrodes is analyzed with nitrogen-adsorption. The result shows that the former has more advantages than the latter. The specific surface area of the former is bigger than that of the latter. The pores of the former are middle-sized, and the average pore diameter is bigger than the efficient radius of hydrated sodium and chloride ion. Scanning electric microscopy (SEM) of the electrodes and the contact angle images of water droplets on the electrodes shows that the former has more pores on the surface and its hydrophilicity is better than the latter. Therefore the charge-discharge performance and the electric adsorption-desalination of the hot-moulded carbon nanotubc electrodes are superior.
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅲ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TB383
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部