纳米结构TiO2/聚3-甲基噻吩多孔膜电极光电化学研究
Photoelectrochemical studies on the nanostructured TiO2/pmet film electrode
【Author】 HAO Yan-zhong, WU Wen-jun(College of Science,College of Chemical & Pharmaceutical Engineering, HeBei University of Science andTechnology, Shijiazhuang 050018, China)
【机构】 河北科技大学理学院； 河北科技大学化学与制药工程学院；
【摘要】 用光电流作用谱、光电流-电势图等光电化学方法研究了ITO/聚3-甲基噻吩(PMeT)膜电极和ITO/TiO2/PMET复合膜电极的光电转换性质.结果表明,PMET膜导带位置为-3.44eV,禁带宽度为1.93eV.修饰ITO/TiO2电极可使光电流发生明显的红移,从而提高了宽禁带半导体的光电转换效率.
【Abstract】 The photon-current conversion properties of nanostructured TiO2/PMET film electrode were studied by using the photocurrent action spectra, the photocurrent dependence of potential and UV-Vis absorption spectra. The bandgap of PMET film was 1.93eV. The diagram of energy level of PMET film was determined with cyclic voltamogramm and photoelectrochemical method. The conduction band of PMET film was -3.44eV. The nanostructured TiO2/PMET film electrode can enlarge the visible optical absorption region and obviously increase the photocurrent in visible region. The photocurrent threshold shifts to >600nm, thus the photon-electron conversion efficiency can be improved .
【Key words】 nanostructured TiO2/PMET electrode； photoelectrochemistry； conducting polymer；
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅲ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TM914
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部