锂离子电池正极材料锂镍复合氧化物的合成及性能研究
Synthesis and performance of lithium nickel oxides as cathode for Li-ion batteries
【Author】 HU Chen, LIU Han-xing, GAN Xiao-yan, OU YANG Shi-xi(State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University ofTechnology, Wuhan 430070, China)
【机构】 武汉理工大学材料复合新技术国家重点实验室；
【摘要】 对LiNiO2派生物LiNixCo1-xM0.05O2(M=Al,Mn,Ti)的性能进行了研究.采用了溶胶-凝胶法(Sol-gel)合成了LiNixCo1-xM0.05O2(M=Al,Mn,Ti),采用XRD表征其晶体结构,均为层状结构;采用扫描电镜(SEM)观察产物的晶体形貌,粉末颗粒细小,粒径约为0.3-0.5μm.充放电测试表明,合成的LiNixCo1-xAl0.05O2的循环性能比较好,LiNi0.7Co0.25Mn0.05O2的初始容量较高.
【Abstract】 Synthesis and Performance of derivative LiNixCo1-xM0.05O2(M=Al, Mn, Ti) were studied.LiNixCo1-xM0.05O2 (M=Al, Mn, Ti) power was synthesized by sol-gel method. XRD results showed that the powders are highly crystallized LiNixCo1-xM0.05O2 with ordered layer structure of α-NaFeO2. SEM micrographs showed the powders are tiny particulate with the particle size of 0.3-0.5 μm. Electrochemical test proves that the cycle property of LiNixCo1-x Al0.05O2 was excellent and the first discharge capacity of LiNi0.7Co0.25 Mn0.05O2 was higher.
【Key words】 lithium ion battery； cathode material； LiNixCO1-xM0.05O2(M=Al, Mn, Ti)；
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅲ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TM911
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部