导热型硅橡胶电子灌封杂化材料研究
Research on silicone rubber hybrid materials with heat conductive performance used for electronic encapsulation
【Author】 GE Jian-fang, JIA De-min (College of Material Science and Engineering, South China University of Technology, Guangzhou 510640, China)
【机构】 华南理工大学材料科学与工程学院；
【摘要】 用不同的进料工艺,以六甲基二硅氧烷、四甲基二乙烯基二硅氧烷和硅酸四乙酯为原料,合成一种反应型SiO2单体。由连续进料工艺得到的SiO2单体,羟基含量低,可使硅橡胶的拉伸强度提高10-11倍,击穿强度升高4kV·(mm)-1左右。在硅橡胶-SiO2-Al2O3杂化材料体系中,引入偶联剂3-MPS,有助于α-Al2O3与硅橡胶间界面作用的增强。
【Abstract】 One reactive monomer was prepared from hexamethyldisiloxane, divinyltetra- methyldisiloxane and tetraethylsilicate etc, in different technology. It was concluded that the hydroxyl content in the monomer was lowered under condition of continuous feed of hexamethyldisiloxane. With this kind of monomer added, the mechanical strength was raised to 10-11 multiples of the unmodified silicone rubber, and electric breakdown strength was elevated about 4kV·(mm)-1. The silicone rubber-SiO2-Al2O3 hybrid materials were prepared, with mechanical properties improved in presence of 3-MPS coupling agent due to the interface action enhancement.
【Key words】 silicone rubber； hybrid material； dielectric； functional materials；
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅲ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TB39
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部