铁磁形状记忆合金CoNiGa马氏体相变特征的研究
Characterization of martensitic transformation in ferromagnetic shape memory CoNiGa alloy
【Author】 MENG Fan-bin, LIU He-yan, QU Jing-ping, LI Song-tao, LI Yang-xian (School of Material Science and Engineering, Hebei University of Technology, Tianjin 300130, China)
【机构】 河北工业大学材料学院；
【摘要】 应用具有变温样品室的X射线衍射仪及扫描电镜研究了铁磁形状记忆合金C050Ni20Ga32样品马氏体相变的特性.研究发现,多晶Co50Ni20Ga32合金具有可恢复的热弹性马氏体转变特性.Y相的存在对马氏体转变的自协作形貌有很大影响.Y相含量多时,马氏体变体的自协作形貌以金刚石形为主,Y相含量少时。马氏体变体的自协作形貌以平行形为主.在大约520℃以上时。Y相的含量随温度升高而增加.
【Abstract】 In this paper, the characterization of martensitic transformation in ferromagnetic shape memory alloy was studied by means of XRD and SEM. The polycrystal Co50Ni20Ga32 alloy possess thermoelastic martensitic transformation effect. The y -phase influence to morphologies of self-accommodation for Co50Ni20Ga32 alloy was observed. In the area abundant y -phase emergence, the surface morphologies of self-accommodation are diamond morphology. In the area few y -phase emergence, the surface morphologies of self-accommodation are parallelogram morphology. Above about 520℃,the quantity of y -phase increase with the increasing of temperature.
【Key words】 shape memory alloy； martensite； morphologies of self-accommodation；
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅲ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TG139
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部