酒石酸络合溶胶-凝胶法制备Ca3CO4O9粉体的研究
Preparation of Ca3Co4O9 powders by the tartaric acid complexing sol-gel method
【Author】 ZHANG Yan-Feng, ZHANG Jiu-Xing, LU Qing-Mei, LIU Yan-qin(The Key Laboratory of Advanced Functional Materials, Ministry of Education. Beijing 100022, China; College of Chemistry, Hebei Normal University, Shijiazhuang 050016, China)
【机构】 北京工业大学新型功能材料教育部重点实验室；
【摘要】 以金属硝酸盐和酒石酸为原料,用酒石酸络合溶胶-凝胶法制备了Ca3Co4O9粉体.分别用TG-DTA、XRD、FT-IR和SEM等手段对干凝胶的热分解过程和Ca3CO4O9的形成过程进行了研究.结果表明:硝酸根离子可以加速凝胶的热分解,在750℃煅烧2h即可得到平均粒径0.6μm的片状Ca3Co4O9粉体.
【Abstract】 Ca3Co4O9 powders were synthesized by the tartaric acid complexing sol-gel method using metal nitrate as raw materials. The pyrolytic decomposition mechanism of the gel and formation process of Ca3Co4O9 was investigated by DTA-TG, XRD, FT-IR and SEM etc. The results show that nitrate ions accelerate the decomposition of the gel, and the platelike Ca3Co4O9 powders with the mean size of 0.6μm can be obtained after the dry gel calcined at 750℃for 2h.
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅲ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TB44
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部