Ba(Mgx/12Ta2x/12Zr（12-3x）/12)O3系统相关系的研究
Study of the phase relation of the Ba(Mgx/12Ta2x/12Zr12-3x/12O3 system
【Author】 OU Jun, WU Bo-lin, ZHONG Lian-yun, DONG Shun-xi (Dept. of Chemical Material and Engineering GuiLin Institute of Technology, Guilin 541004, China)
【机构】 桂林工学院材化系；
【摘要】 目前的文献均表明钽镁酸钡Ba(Mg1/3Ta2/3)O3不易获得单一物相.我们在Ba(Mg1/3Ta2/3)O3结构不变的基础上,研究了Ba(Mgx/12Ta2x/12Zr(12-3x)/12)O3系统的相组成关系.用Zr4+置换Ba(Mg1/3 Ta2/3)O3中的Mg2+和Ta5+离子对,在0<x<4范围内生成P3ml固溶体,在x<3.33时开始出现BaZrO3相,在3.33≤x<4生成P3ml固溶体单一物相.
【Abstract】 The single phase is not easy acquired in Ba(Mg1/3Ta2/3)O3 as the papers so far have showed. The relation between the phases and compositions in Ba(Mgx/12Ta2x/12Zr(12-3x)/12)O3 was investigated on the basis that the structure of Ba(Mg1/3Ta2/3)O3 with Zr4+cation, at the range of 0<x<4 solid solution was produced; when x<3.33 the phase of was formed; and at the range of 3.33≤x<4, single phase of solid solution was prepared.
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅲ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TB34
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部