拉伸速率对PVDF薄膜介电压电性能的影响
Effect of stretching rate on piezoelectric and dielectric properties of PVDF films
【Author】 XU Ren-xin, CHEN Wen, XU Qing, ZHOU Jing, HU Li-xin(Institute of Materials Science and Engineering, Wuhan University of Technology, Wuhan 430070, China; Chemical Engineering Department, Hubei Polytechnic University, Wuhan 430064, China)
【机构】 武汉理工大学材料科学与工程学院； 湖北工学院化学工程系；
【摘要】 通过单轴拉伸工艺制备了PVDF压电薄膜,运用X射线衍射和FTIR分析技术分析了不同拉伸速率下薄膜的微观结构;并探讨了极化电场对薄膜压电介电性能的影响.结果表明:PVDF经单轴拉伸后,体系中出现了压电性能很强的β相和γ相。而且拉伸速率越高,体系出现的β相和γ相越多.随着极化电场的升高,PVDF压电薄膜的压电应变系数升高,介电常数升高,介电损耗降低.
【Abstract】 PVDF piezoelectric films were prepared by uniaxial stretching. The techniques of X-ray Diffraction and FTIR were used to analyze the microstructure of the films stretched under the different rate. The effect of the polarization field on the piezoelectric and dielectric properties of PVDF films was also studied. It is shown that the P and γ phase which provided the good piezoelectric properties to the films emerged in the PVDF system after stretching. Moreover, higher the drawing speed, more the β and γ phase. The piezoelectric strain coefficient and the dielectric constant of PVDF films increased, and the dielectric loss decreased with the increasing of the polarization field.
【Key words】 PVDF； uniaxial stretching； piezoelectric properties； dielectric properties；
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅲ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TB383
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部