The improvement of charge storage life for positively corona charged polytetrafluoroethylene film electrets
【Author】 ZHANG Peng-feng, XIA Zhong-fu, AN Zhen-lian, WU Xian-yong (Pohl Institute of Solid State Physics, Tongji University, Shanghai 200092, China)
【机构】 同济大学波耳固体物理研究所；
【摘要】 研究了栅控恒压正电晕充电后的聚四氟乙烯薄膜驻极体的电荷输运特性,并对其电荷储存稳定性加以改善.结果显示在约100℃以下的较低温区和高于180℃以上的较高温区内慢再捕获效应控制着脱阱电荷的输运:而在100-180℃的温区内由慢再捕获效应过渡为快再捕获效应后再回到慢再捕获效应.经改性后的正、负极性PTFE薄膜驻极体不仅具有相近的电荷储存密度,而且在一定的温度区间内它们的电荷储存和衰减呈现类似的规律.
【Abstract】 In this paper, charge dynamic and improvement of charge storage stability in positively corona charged polytetrafluoroethylene (PTFE) film electrets have been studied. It is found that from room temperature to 100℃ and over 180℃, slow retrapping controls the transport of detrapped charge; however, from about 100℃ to 180℃, the transportation rule is changed from slow retrapping to fast retrapping and finally returning to slow retrapping. The improved positively and negatively corona charged PTFE film electrets not only have a comparable charge storage density but also similar rule for their charge storage and decay in certain temperature region.
【Key words】 polytetrafluoroethylene； positive charge stability； detrapped charge；
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅲ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TB34
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部