液相沉淀法制备球状Bi2O3粉料
Preparation of spherical Bi2O3 powder by precipitation process
【Author】 CHEN Pei-rong, JI You-zhang, FENG Shi-fen (Institute of Plasma Physics, Academia Sinica, Hefei 2300031, China)
【机构】 中国科学院等离子体物理研究所；
【摘要】 以金属铋为原料,溶解在硝酸中,配置成Bi(NO3)3溶液,用NH3-NH4HCO3作沉淀剂,调节pH值,制备Bi2O3粉料.通过控制反应温度、加料速度、反应时间以及加入适量的分散剂,制备得粒径为2—3μm、粒度分布均匀、分散性良好的超细球状Bi2O3粉料.用Bi2O3粉料制备的znO压敏电阻,具有压比低,方波冲击合格率高,性能一致等优点.
【Abstract】 The starting metal bismuth dissolves in nitric acid to form the solution of Bi(NO3)3. A aqueous NH3-NH4HCO3 solution is added in order to adjust the pH of the bismuth ions(Bi3+) solution within a range, so that bismuth subcarbonate precipitates. Bi2O3 powder is obtained by calcination. The micrograph of the Bi2O3 powder can be controlled during the precipitation process through the reaction temperature, the rate of addition of the precipitation reagent, the reaction time and the amount of the dispersant. Accordingly, spherical Bi2O3 powder with diameters ranging from 2μm to 3 μm is prepared. The spherical Bi2O3 particles have such advantages as uniform size distribution and excellent dispersing property. ZnO varistors made from the resulting powder exhibit properties of low discharge voltage ratio, great eligibility coefficient measured by a rectangle wave of 2ms 800A and good stability in the above characteristics.
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅲ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TB44
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部