SrBi4Ti4O15高取向铁电陶瓷制备与性能研究
Study on processing and performance of highly-oriented ferroelectricsceramics SrBi4Ti4O15
【Author】 HAO hua, LIU Han-xing, HU Shui-tang, OUYANg Shi-xi(1. Material Science and Engineering Department, Wuhan University of Technology, Wuhan 430070, China;2. State Key Laboratory of Advanced Technology for Materials Synthesis and Processing,Wuhan University of Technology, Wuhan 430070, China)
【机构】 武汉理工大学材料学院硅酸盐教育部国家重点实验室； 武汉理工大学材料复合新技术国家重点实验室；
【摘要】 用熔盐法和固相法合成SrBi4Ti4O15粉体,对其微观形貌进行了对比.熔盐法合成的粉体片状结构明显,合成温度低,比固相合成合成温度低50℃,一定程度上避免了Bi2O3的挥发.热压烧结的SrBi4Ti4O15陶瓷在(001)面取向非常明显,其压电性能也得到提高.
【Abstract】 SrBi4Ti4O15 powder was synthesized by conventional synthesis method (CS) and molten salt synthesis method (MSS).Comparing the different methods, plate-like form of MSS powder was more distinct and the synthesis temperature of MSS was lower. This can avoid the volatilization of Bi2O3. The sintered samples of MSS had grain orientation at (0,0,10) plane. The degree of (0,0,10) grain orientation F was 62.1%. Hot pressing made (0,0,10) grain orientation more distinct (F=85.7%). The piezoelectric performance of sample sintered by hot pressing was improved.
【Key words】 molten salt synthesis； hot pressing sinter； grain orientation degree；
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅲ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TQ174
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部