多孔PTFE/P(VDF-HFP)复合膜的驻极体性质
Electret properties for hybrid films composed of porous PTFE andP(VDF-HFP) film
【Author】 WANG Fei-peng, XIA Zhong-fu, AN Zhen-lian, WU Yue-hua, SHEN Jun (Pohl Institute of Solid State Physics, Tongji University, Shanghai 200092, China)
【机构】 同济大学波耳固体物理研究所；
【摘要】 通过栅控恒压负电晕充电、等温表面电位衰减测量、热刺激放电(Thermally Stimulated Discharge,TSD)电流谱分析、电荷TSD和压电D33系数测量等方法,首次研究了将旋涂在基片上的含一定溶剂的聚偏氟乙烯和六氟丙烯共聚物(P(VDF-HFP))薄膜与多孔聚四氟乙烯薄膜均匀压合形成的多孔PTFE/P(VDF-HFP)双层复合膜系的驻极体性质。从多孔PTFE面充电的双层膜具有较从P(VDF-HFP)面充电优异的多的电荷热稳定性。使用介电谐振谱测量的双层膜的压电d33系数(31pC/N)是传统的铁电聚合物材料PVDF相应值(15 pC/N)的2倍左右。
【Abstract】 By negative corona charging with a grid, measurements of isothermal surface potential decay, thermally stimulated discharge current spectra (TSD), charge TSD, and measurements of piezoelectric d33 coefficient by dielectric resonance spectroscopy, the electret properties of the double layer hybrid films composed of porous PTFE and spin coated P(VDF-HFP) film are first studied. The space charge stability of the film charged at the side of porous PTFE is better than that charged at the side of P(VDF-HFP). The film electret has two times high piezoelectricity (d33=31pC/N) than PVDF (d33=1 5pC/N).
【Key words】 porous PTFE； P(VDF-HFP)； electret； piezoelectricity；
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅲ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TB383
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部