纳米氧化锌半导体块材晶粒生长的研究

Grain growth of nano-sized semiconductor ZnO bodies

推荐 CAJ下载
PDF下载
不支持迅雷等下载工具，请取消加速工具后下载。

【Author】 QIN Xiu-juan, SHAO Guang-jie, WANG Wen-kui, LIU Ri-ping( Department of Environmental and Chemical Engineering, YanShan University, Qinhuangdao 066004, China; Key Laboratory of Metastable Materials Science and Technology, Qinhuangdao 066004, China)

【机构】燕山大学环境与化学工程系；河北省亚稳材料制备技术与科学重点实验室；

【摘要】以平均粒径20nm的ZnO超微粉为原料,研究了纳米ZnO块材烧结过程中的晶粒生长行为,由实验结果得出:在700～900℃温度范围内,纳米ZnO烧结的晶粒生长动力学指数n为6,晶粒生长的表观活化能Q为64kJ/mol,导出了纳米ZnO的晶粒生长动力学方程。与粗晶ZnO的晶粒生长进行了对比,初步分析了纳米ZnO的烧结机制。更多还原

【Abstract】 Grain growth in sintered nano-sized ZnO bodies was studied on based of ZnO nanoparticles with average diameter 20nm. The results showed that the grain growth kinetic exponent n value was observed to be 6 while the apparent activation energy was 64kJ/mol form 700℃ to 900℃ in air. Kinetic equation of ZnO grain growth was given. Compared with coarse crystalline ZnO, whose grain growth kinetic exponent n value was 3 and the apparent activation energy was 220kJ/mol form 1000℃ to 1400℃ in air. Preliminary explainations are given to above results.更多还原

【关键词】纳米烧结； ZnO纳米块材；晶粒生长的动力学指数；表观活化能；
【Key words】 nanosintering: nano-sized ZnO bodies； grain growth kinetic exponent； apparent activation energy；

【基金】燕山大学科技发展基金的资助(YDJJ2031)

【会议录名称】第五届中国功能材料及其应用学术会议论文集Ⅲ

【会议名称】第五届中国功能材料及其应用学术会议

【会议时间】2004-09
【会议地点】中国北京·秦皇岛
【分类号】TN304

【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部

知网节下载

节点文献中：

本文链接的文献网络图示:

本文的引文网络

节点文献