W/WO3pH电极的制备以及表面膜微观分析研究
Preparation of W/WO3 pH electrode with a method of sol-gel and itssurface film micro-analysis
【Author】 CHEN Dong-chu, WANG Zhe, ZHEN Jia-sheng, FU Chao-yang (Chemistry Department, Huazhong University of Science and Technology, Wuhan 430074, China)
【摘要】 利用离子交换法制备了WO3的Sol溶液,并应用于H+选择性电极的敏感膜。电极有良好的H+响应,响应pH值范围为2-11,响应灵敏度约为52mV/pH。本文利用TG、DSC、IR、SEM、AFM、XRD等分析手段对WO3膜的组成与形态进行了表征,WO3形貌为龟裂泥土状,膜的组成为WO3、WO3·H2O或WO3·0.33H2O,随着热处理温度的提高,结晶水减少。EIS图谱表明电极的H+响应动力学过程为H+扩散过程控制,H+扩散系数为10-10cm2·S数量级。
【Abstract】 The WO3 Sol was prepared with a method of ion-exchange, and the Sol was applied to fabricating H+ selective film; the response sensitivity of the prepared W/WO3 electrode changes from 37mV/pH to 52mV/pH in the pH range of pH2-11; many kinds of determination technology, such as TG,DSC,IR,SEM,AFM,XRD were used to the characterization of the film; it was found that the film was like crack dried mud, and the film was composed of WO3、 WO3 ·H2O or WO3 ·0.33H2O; the hydrate water decreased with the increment of the treated temperature; the H+ response course was controlled by the H+ diffusion from the solution to the WO3 crystal, which was indicated in the spectra of the EIS; the H+ diffusion parameter in the course of H+ response for this W/WO3 electrode was about 10-10cm2 · S ; the best treated temperature here was 200 ℃.
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅲ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TB34
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部