Li2O～SiO2～V2O5～SnO2体系的锂快离子导体研究
The study of Li2O-SiO2-V2O5-SnO2 lithium fast ion conductor system
【Author】 HUANG Geng, WANG Wen-ji (New Technical Materials Research Institute Fuzhou University, Fuzhou 350002, China)
【机构】 福州大学新技术材料研究所；
【摘要】 Li2O-SiO2-V2O5-SnO2四元体系固溶体是锂离子/电子混合导体,本文用均匀试验设计方法研究其电导率随组分的变化规律,寻找电导率最高的配方区域。在选取的试验点中分析了其中的离子和电子电导率的大小比例。选取试验点验证了高电导率区域的电导率变化规律。实验中获得的室温离子电导率最高的快离子导体为2.06×10-4/cm.
【Abstract】 In order to prepare the highest ionic conductor of Li2O-SiO2-V2O5-SnO2 system. The optimal ratio of starting materials Li2O:SiO2: SnO2:VO2.5 has been designed by Uniform Design. The result is match the estimate value. The ratio between electron and ion conductivity has been researched. The highest ambient ion conductivity is 2.06×10-4S/cm for the above lithium fast ion conductors system., the electronic conductivity is 3 orders of magnitude lower than the ionic conductivity.
【Key words】 lithium fast ion conductor； uniform design； ionic conductivity； electronic conductivity；
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅲ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TM911
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部