Gd2O3掺杂CeO2-δ固体电解质的电化学性能研究
Electrochemical performance of Gd2O3 doped CeO2-δ electrolyte
【Author】 SONG Xi-wen, Zhao YONG-wang, PENG Jun, ZHAO Wen-guang, AN Sheng-li( School of Metallergy, University of Science and Technology Beijing, Beijing 100083, China; School of Material Science and Technology, Inner Mongolia University of Science and Technology,Baotou 014040, China)
【机构】 北京科技大学冶金学院； 内蒙古科技大学材料科学与工程学院；
【摘要】 利用交流阻抗技术(EIS)测试了Gd2O3掺杂CeO2-δ固体电解质的电导率。当测试温度低于695℃时,阻抗谱由2个变形的半圆弧组成;而高温时仅有1个变形的半圆弧。固体电解质的晶格电导率、晶界电导率和总电导率与测试温度的关系服从Arrhenius公式。材料的电导率随成型压力的增大先增大,然后减小。随烧结温度的升高,材料电导率是升高的。
【Abstract】 The a.c conductivity measurements of Gd2O3 doped CeO2-δ electrolyte was performed using a Solatron 1260 frequency response analyzer. Typical impedance spectra consist of two depressed semicircles at low testing temperature and one depressed semicircle at elevated testing temperature. The relationships between the conductivities and temperature can be expressed as Arrhenius equation. As the compacting pressure improves, the conductivities increase firstly and then decrease. The conductivities improve with increasing sintering temperature.
【Key words】 doped ceria； ionic conductivity； solid electrolyte； AC impedance spectra；
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅲ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TM911.4
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部