SnSb0.18合金的电化学性能研究
Studies on electrochemical properties of SnSb0.18 alloy
【Author】 SHU Jie, CHENG Xin-qun, SHI Peng-fei (Department of Applied Chemistry, Haerbin Institute of Technology, Haerbin 150001, China)
【机构】 哈尔滨工业大学应用化学系；
【摘要】 以化学还原法制备了SnSb0.18合金,并对合金的成分、组成及形貌等进行了分析;对合金的嵌脱锂性能研究发现,SnSb0.18合金能与锂形成多种合金,具有良好的嵌脱锂性能,首次循环的库仑效率为74.7%,放电容量可达到611mAh·g-1。研究中还发现热处理能有效地提高电板的循环寿命,增大放电容量,合金电极在氩气保护、300℃温度下处理2h,其40次循环之后比容量仍能保持在440 mAh·g-1。
【Abstract】 SnSb0.18 alloy prepared by chemical reduction was examined with X-ray diffraction, energy diffraction spectroscopy and scanning electron microscope. Electrochemical properties of SnSb0.18 alloy has been tested by constant current cycling、 cyclic voltammetry and AC impedance. SnSb0.18 alloy reacts reversibly with Li and shows good performance. Coulombic efficiency of 74.7% and specific capacity of 611mAh· g-1 can be achieved in the first cycle. We also find that the electrode which was annealed at 300℃ for 2h under argon atmosphere showed better cycle performance than the electrode without heattreatment. After 40 cycles the heat-treated electrode can deliver high discharge capacity of 440mAh· g-1.
【Key words】 SnSb0.18 alloy； performance of intercalation and deintercalation； cycle life； specific capacity；
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅲ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TG113
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部