NixCo4-xSb12化合物的制备及热电性能研究
Preparation and thermoelectric properties of NixCo4-xSb12 compounds
【Author】 ZHANG Long, ZHANG Jiu-xing, LU Qing-mei, LIU Ke-gao(Key Laboratory of Advanced Functional Materials, Ministry of Education, Beijing University ofTechnology, Beijing 100022, China)
【机构】 北京工业大学新型功能材料教育部重点实验室；
【摘要】 以Ni作为添加元素,利用放电等离子技术制备了NixCo4-xSb12(x=0-0.35)化合物热电材料。通过先进的性能表征手段,深入探讨了NixCo4-xSb12化合物的热电性能,为n型热电材料的研究提供了有价值的参考。实验结果表明,一定量Ni的添加,能有效改善材料热电性能,提高热电优值;在Ni添加量x=0.2时,Ni0.2Co3.8Sb12化合物在温度T=773K时具有最大的热电性能优值ZTmax=0.45.
【Abstract】 The structure and thermoelectric properties of filled skutterudite compounds of NirCo4-xSb12(x=0-0.35), doped by Ni, which were prepared through spark plasma sintering, were investigated by accurate apparatus. All samples showed n-type conduction. Ni doped can decrease electrical resistivity, Seebeck coefficient and thermal conductivity. So as to improving ZT value. The maximum ZT value of 0.45 was obtained at 773K with Ni0.2Co3.8Sb12.
【Key words】 n-type thermoelectric materials； skutterudite compound； Ni substitution； spark plasma sintering；
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅲ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TB39
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部