恒定电压下微弧氧化陶瓷膜电学性质的研究
Study on electrical properties of MAO coatings fabricated at constant voltage
【作者】 吴汉华； 汪剑波； 李俊杰； 王秀琴； 金曾孙； 李哲奎；
【Author】 WU Han-hua, WANG Jian-bo, LI Jun-jie, WANG Xiu-qin, JIN Zeng-sun, LI Zhc-kui (State Key Laboratory for Superhard Materials, Jilin University, Changchun 130012, China;College of Physics, Jilin University, Changchun 130021, China; Department of Physics, Yanbian University, Yanbian 133000, China)
【机构】 吉林大学超硬材料国家重点实验室； 延边大学物理系；
【摘要】 利用自制的数据采集系统研究了恒定电压下铝合金交流微弧氧化陶瓷膜形成过程中电学性质的变化规律。实验结果表明,微弧氧化过程中阴、阳极的峰值电流明显分为5个不同阶段;陶瓷膜形成过程中的动态正向电阻和电阻率随处理时间分阶段变化,而动态的反向电阻和电阻率变化不大。在微弧氧化过程中,各时刻的动态正,反向电阻值不同,一般情况下,动态正向电阻远大于反向电阻。
【Abstract】 The electrical properties during fabricating MAO coatings were studied by means of a self-made data collecting system. The experimental results showed that the variations of the cathodic and anodic current amplitude and average working current with treatment time included obviously five different stages, and the variations of coatings’ dynamic positive resistance and resistance rate include different stages, too, while the variations of dynamic negative resistance and resistance rate with oxidation time were unobvious. During MAO process, the dynamic positive resistance at any time was not equal to the negative resistance, and the dynamic positive resistance was more than the negative resistance in general.
【Key words】 aluminium alloy； microcarc oxidation； electrical property； ceramic coating；
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅱ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TB43
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部