新型耐高温聚酯PCT的等温结晶性能研究

Study on isothermal crystallization behavior of newly developed high temperature resistant polyester PCT

推荐 CAJ下载
PDF下载
不支持迅雷等下载工具，请取消加速工具后下载。

【Author】 YU Ai-fang, JIANG Yu, LI Wen-gang, HUANG Xiang-an(State Key Laboratory for Modification of Chemical Fibers and Polymer Materials,Donghua University, Shanghai 200051, China)

【机构】东华大学纤维材料改性国家重点实验室东华大学材料学院；

【摘要】聚对苯二甲酸1,4环己二甲醇酯(PCT)是一种新型的耐高温聚酯。用差示扫描量热法(DSC)分析了PCT的等温结晶性能,并进行了等温结晶动力学分析。结果表明,PCT比PET的结晶速度快;动力学计算表明,PCT在较高温度下的结晶以异相成核为主。更多还原

【Abstract】 Poly(ethylene terephthalate-co-1,4-cyclohexylene dimethylene terephthalate) (PCT) is a newly developed high temperature resistant polyester. Isothermal crystallization behavior of PCT was analyzed by Differential Scanning Calorimeter (DSC), and kinetic analysis of isothermal crystallization between PET and PCT was compared. The results showed that PCT could be more easily crystallized than PET, and the kinetic analysis of isothermal crystallization revealed that PCT mainly included heterogeneous nucleation at higher temperature.更多还原

【关键词】聚对苯二甲酸环己二甲醇酯(PCT)；耐高温聚酯；等温结晶性能；
【Key words】 poly(ethylene terephthalate-co-1,4-cyclohexylene dimethylene terephthalate)(PCT)； high temperature resistance polyester； isothermal crystallization Behavior；

【会议录名称】第五届中国功能材料及其应用学术会议论文集Ⅱ

【会议名称】第五届中国功能材料及其应用学术会议

【会议时间】2004-09
【会议地点】中国北京·秦皇岛
【分类号】O631

【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部

知网节下载

节点文献中：

本文链接的文献网络图示:

本文的引文网络

节点文献