Cu-Zn-Al合金纳米分叉结构的制备及显微分析
Preparation and TEM study of branded nano-structure of Cu-Zn-Al alloy
【Author】 GAO Hou-xiu, CHEN Quan-shui, LIU Shuang-yi, ZHANG Gui-jie, YANG Yu-qin( School of Material Science and Engineering, Tianjin University, Tianjin 300072, China; Department of Material Science and Engineering, East China Technology Institute, Fuzhou 344000, China)
【机构】 天津大学材料科学与工程学院；
【摘要】 通过对Cu-Zn-Al合金进行简单的化学处理,得到了具有分又结构的Cu-Zn-Al合金纳米结构,用透射电镜考察了分叉纳米结构的形貌及其微结构特征。实验表明:分叉纳米结构的形态与化学处理工艺有关,有的分支纳米结构与未分支的形态类同,分支的顶端呈开口状态;有的沿生长方向呈规则的同向排列,各分支的形态相近,端部呈封闭状态。Cu-Zn-Al合金纳米分叉结构的形成可能与制备条件的扰动有关,对Cu-Zn-Al合金纳米结构的分又生长机制进行了初步探讨。
【Abstract】 In substrate of Cu-Zn-Al alloy, branch structure of one dimensional nano-material was prepared by simple chemical method, and its pattern and microscopic structure were investigated by TEM. The shape of the branches was related to disposed technics. Some is similar to natural nano-structures, and the top was open naturally, Others grow in common direction, all shape of the branches were resemble, and the top was close. In this paper the topographic defects related to the branches and the growth mechanism of branch structure of one dimensional nano-material of Cu-Zn-Al alloy was preliminary discussed.
【Key words】 one dimensional nano-structure； Cu-Zn-Al alloy； branch； TEM；
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅱ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TB383
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部