金属Ag对NiFe2O4尖晶石性能的影响
Effect of Ag on properties of NiFe2O4 spinel
【Author】 ZHANG Shu-ting, YAO Guang-chun, LIU Yi-han, XI Jin-hui (College of materials & metallurgy, Northeastern University, Shenyang 110004, China)
【机构】 东北大学材料与冶金学院；
【摘要】 制备了不同金属Ag含量的Ag-NiFe2O4金属陶瓷,利用扫描电子显微镜观察显微组织,由X射线衍射分析化学成分,研究了Ag的添加量对其体积密度、气孔率、热震性、导电率以及腐蚀速率的影响,试验结果表明,抗热震性和导电能力随着Ag含量的增加而增强,导电率的提高和腐蚀率的增大仍是一对突出的矛盾。单一通过添加金属Ag不可能使导电率和腐蚀率都满足要求。
【Abstract】 The several kinds of Ag-NiFe2O4 cermets with different mass percent of Ag have prepared. Microstructural changes were observed by scanning electronic microscope and composition was determined with x-ray detector. Effect of different content of Ag on the density, property of thermal shock, conductivity and corrodent rate were tested. The results showed that the thermal shock performance and conductivity have improved in company with the addition of content of Ag. Corrodent rate and conductivity impossibly meet a demand by adding Ag at the same time.
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅱ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TB39
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部