微波加热制备尺寸各向异性纳米金属钌颗粒
Preparation of anisotropic Ru nanoparticles by microwave-polyol process
【作者】 赵鹏； 姚燕燕； 田晓珍； 许启明； A.Gedanken；
【Author】 ZHAO Peng, YAO Yan-yan , TIAN Xiao-zhen, XU Qi-ming, A. Gedanken( Institute of materials science & engineering, Xi’ an University of Architecture & Technology, Xi’an 710055, China; Department of Chemistry, Bar-Han University, Ramat-Gan 52900, Israel)
【机构】 西安建筑科技大学材料学院； Department of Chemistry Bar-Ilan University Ramat-Gan 52900 Israel；
【摘要】 采用微波加热Polyol法以PVP作为稳定剂,首先快速合成了晶粒尺寸为2-6nm具有不同长宽比的各向异性的单分散金属钌胶体颗粒。以单分散胶体颗粒为晶种,获得不同团聚程度的纳米金属钌颗粒。高分辨电子显微镜(HRTEM)研究表明,树枝状纳米金属钌是由随机取向的金属钌单晶颗粒组成的.
【Abstract】 A colloidal solution of monodispersive anisotropic Ru metal nanoparticles (2-6nm mean panicle size) with different aspect ratios was obtained firstly by using microwave irradiation. Particles with different degrees of agglomeration have been also synthesized by using monodispersive particles as seeds and PVP (Poly N-vinyl-2-pyrrolidone) as stabilization reagent. The HRTEM images indicated that dendritic particles formed by controlling agglomeration consist of single-crystal domains with random crystalline orientation.
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅱ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TB383
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部