超声波作用下金红石型TiO2枝蔓晶的形成
Sonochemical synthesis of rutile titanium dioxide dendrite crystal
【Author】 GUO Wei-lin, WANG Xi-kui (Chemistry and Chemical Engineering College, Ji’nan University, Ji’nan 2S0022, China)
【机构】 济南大学化学与环境工程学院；
【摘要】 在超声波作用下,以四氯化钛为前驱体于较低温度下直接制备出金红石型纳米二氧化钛,所得二氧化钛晶粒为长柱状,大小约为3/12nm(W/L),并且晶粒取向连生,聚集形成枝蔓晶,该聚集体为羽状,利用XRD、TEM、TG-DTA等手段对其进行表征,最后对在超声作用下二氧化钛的形成机理进行了讨论.
【Abstract】 A new sonochemical method to directly prepare rutlie nanocrystalline TiO2 has been established. TiO2 particles were synthesized by the hydrolysis of TiCl4 under high-intensity ultrasonic irradiation at 70℃ for 3h. Characterization was accomplished using various different techniques, such as powder X-ray diffraction (XRD), transmission electron microscopy (TEM), selected area electronic diffraction (SAED) and thermogravimetry -differential thermal analysis (TG-DTA). The TEM images showed that the particles of TiO2 were columnar in shape and the average sizes were ca. 3/12nm(W/L). The particles were linked together each other at the certain principle, forming the shape like dendrite crystal. The formation mechanism of rutile TiO2 dendrite crystal under high-intensity ultrasonic irradiation was also discussed. The crystal structure of products was depended upon the polymerized form of Ti4+ in solution.
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅱ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TB383
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部