热等静压方法制备蓝青铜K0.3MoO3多晶材料
Preparation of the Blue bronze polycrystalline material K0.3MoO3 by HIP method
【Author】 WANG Jun-feng, JIA Ying, KE Man-zhu, SHI Jing, JIN Zheng-zhong(Department of Physics, Wuhan University, Wuhan 430072, China; The State Key Lab of Advanced Material andProcessing; Wuhan University of technology, Wuhan 430070, China)
【机构】 武汉大学物理科学与技术学院； 武汉理工大学国家新材料重点实验室；
【摘要】 钼蓝青铜A0.3MoO3(A为K,Rb或Tl)是一类典型的低维材料,由于它们具有与电荷密度波(CDW)、自旋密度波(SDW)及超导相联系的奇异性质。因而受到了人们广泛的关注.长期以来对蓝青铜的研究主要在单晶上开展,本文则采用热等静压方法成功制备出了钾蓝青铜多晶材料,对于蓝青铜薄膜应用中时靶材的制备有实际意义.电阻温度关系曲线的测量显示,钾蓝青铜K0.3MoO3在180K附近发生导体到半导体的Peierls相变.
【Abstract】 Owning to many interesting physical properties associated with charge-density-wave (CDW) and spin-density-wave (SDW) phenomena, the molybdenum blue bronzes A0.3MoO3 (A=K, Rb, Tl) have been followed with sustained interest during the past decades. In this paper, we have successfully prepared the blue bronze polycrystalline material K0.3MoO3 by Hot Isostatic Pressing (HIP) method. The temperature dependence of resistance reveals that this compound undergo Peierls phase transition near 180K.
【Key words】 low-dimensional material； charge density wave； hot isostatic pressing: preparation；
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅱ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TB383
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部