纳米复合Al-Ni-Y系铝合金的制备技术
Fabrication of Al-Ni-Y Al alloy with nanoscale composite structure
【Author】 GUO Sheng, LIU Yong, LIU Zu-ming, HUANG Bai-yun (State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083, China)
【机构】 中南大学粉末冶金国家重点试验室；
【摘要】 部分晶化非晶铝合金因其优异力学性能备受关注,对块体非晶铝合金制备技术的研究意义重大.本工作通过紧耦合惰性气体雾化技术制备了Al82Ni10Y8非晶及纳米晶粉末,随后利用超高压固结成形技术对雾化粉末进行致密化。制备所得的块体材料获得了非晶及纳米晶的复合结构,利用差示扫描量热分析,X射线衍射,扫描电镜和透射电镜等测试手段对合金的热稳定性,物相组成,微现组织和形貌进行了分析,并探讨了合金的可能致密化机理.
【Abstract】 Partially crystallized Al-based amorphous alloys arouse much interest for their excellent mechanical properties. Investigation on fabrication of bulk forms of amorphous Al alloys is of great significance. In the present work, amorphous and nanocrystalline Al82Ni10Y8 powders were firstly prepared by close-coupled inert gas atomization then consolidated under ultrahigh pressure. The bulk materials were found to have a dual-phase nanoscale composite structure. Differential scanning calorimetry (DSC), X-ray diflractometry (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM) methods were carried out to analyze the thermal stability, phase composition and microstructure. Also included were possible densification mechanisms.
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅱ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TB383
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部