常温常压下Cu-Zn-Al合金一维纳米结构的制备
Preparation of one dimensional nano-structures of Cu-Zn-Al alloy at normal temperature and pressure
【Author】 GAO Hou-xiu, LIU Shuang-yi, CHEN Quan-shui, ZHANG Gui-jie, LI Gui-jie( School of Material Science and Engineering, Tianjin University, Tianjin 300072, China; Department of Material Science and Engineering, East China Technology Institute, Fuzhou 344000, China)
【机构】 天津大学材料科学与工程学院；
【摘要】 常温常压下,以Cu-Zn-Al合金为基体,经过适当的混和酸处理,制得了几种形貌和结构不同的一维合金纳米结构,通过能量弥散X射线(EDX)分析表明它们的主要成分是Cu、Zn、Al,其直径一般在20-50nm左右,最长长度达1600nm.合金中存在的非线性振荡,以及酸处理后产生纳米粒子是生成一维合金纳米机构的关键.结合透射电子显微镜照片初步分析了一维合金纳米结构的生长机制并给出了生长模型.
【Abstract】 In normal temperature and pressure, several kinds of one dimensional nano-structure with different patterns and structures whose substrate is Cu-Zn-Al alloy were successfully prepared after treated by mixed acid. The spectrum of EDX showed that main ingredients of them were Cu, Zn and Al. Most of their diameters were 20-50 nm, and their biggest length was about 1600nm. It is the non-liner oscillation of Cu-Zn-Al alloy and nanoparticles produced after acid treatment that play the pivotal role in the preparation of alloy nano-structures. The growth mechanics of nano-structures were primarily studied by making use of TEM photos, and the growth model was also put forward.
【Key words】 Cu-Zn-Al alloy； one dimensional nano-structure； nanoparticals； growth mechanics；
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅱ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TB383
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部