节点文献
功能化纳米晶与聚醚的分子组装
Molecular assembly of functionalized nanocrystal and polyether
【Author】 SHEN Yong-feng, CHEN Su, CHEN Li (School of Chemistry and Chemical Engineering, Nanjing University of Technology, Nanjing 210009, China)
【机构】 南京工业大学化学化工学院；
【摘要】 以醋酸镉和硫脲为原料,巯基乙醇为有机配体,制备了粒径可控的,表面富有羟基的CdS纳米晶.表面的羟基与γ-(2,3-环氧丙氧)丙基三甲基硅烷发生缩合反应,得到功能化的CdS纳米晶粉末在双金属催化剂的存在下,与环氧丙烷进行开环聚合,制备出分子组装的CdS纳米晶/聚醚接枝共聚物.用TEM表征了CdS纳米晶的形貌,紫外-可见光吸收光谱测定了纳米晶的光学性能,FT-lR证实了有机物在纳米晶表面的接枝.
【Abstract】 Cadmium acetate and thiourea were employed to prepare particle size controlled CdS nanocrystals, which contains hydroxyl group. The grafted hydroxyl group on CdS nanocrystal surface could react with 3-Glycidoxypropyltrimethoxysilane (GPTS), and the functionalized CdS nanocrystal/polyether graft copolymer was obtained by the functionalized CdS nanocrystal grafting with propylene oxide (PO) via ring open polymerization under the DMC catalyst. TEM was used to characterize its morphology and UV-vis spectra was employed to characterize its optical properties. FT-IR spectra results confirmed the possibility of various organic monomers grafted on the surface of nanocrystal.
【Key words】 CdS nanocrystal； organic ligand； 3-Glycidoxypropyltrimetboxysilane； propylene oxide； polyether；
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅱ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TB383
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部