阳极氧化制备TiO2纳米多孔膜
Preparation of nano-porous TiO2 film by anodic oxidation
【Author】 WANG Wei, TAO Jie, TAO Hai-jun, WANG Ling (College of Material Science and Technology. Nanjing University of Aeronautics and Astronautics, Nanjing. 210016, China)
【机构】 南京航空航天大学材料科学与技术学院；
【摘要】 分别在氢氟酸和硫酸两种电解液体系下对纯钛(TA1)试样进行阳极氧化,在钛的表面获得TiO2纳米多孔膜.利用膜的颜色的不同来判断膜的厚度的变化,用FESEM观察了孔的形貌和结构并用XRD测试了TiO2膜的晶型,进而研究了阳极氧化电压对孔径和多孔膜晶型的影响并对多孔膜的形成机理进行了阐述.
【Abstract】 In this experiment, nano-porous TiO2 film was prepared on pure titanium (TA1) by anodic oxidation in two electrolytes which are hydrofluoric acid and sulfuric acid. Accord to the color of the different films, the diversification of the films’ thickness was estimated. Observing the structure of the nanopores by FESEM and testing the crystal structure by XRD, the effect of the anodization voltage on the diameter of pores and the crystal structure was investigated. Finally, the forming mechanism of the porous film was discussed.
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅱ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TB383
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部