掺入纳米级含硅微粒的复合铝氧化膜耐蚀特性研究
Study on corrosion resistance property of composite anodic aluminum film mix into nanometer silicon
【Author】 LIANG Yan-ping, LU Min, WANG Li-xian(1.School of Science, Xidian University, Xi’an 710071 China;2. Department of Chemical Engineering, Shanghai Institute of Technology, Shanghai 20023S, China)
【机构】 西安电子科技大学理学院应用化学系； 上海应用技术学院化学工程系；
【摘要】 采用电化学途径,通过铝合金在一次电解、二次电解过程中,掺入纳米级的含硅微粒,制备掺硅复合铝氧化膜.借助于先进的结构和性能表征手段,探讨了掺硅复合铝氧化膜的结构、组成及耐蚀机理.对膜层进行了盐雾、霉菌.高温、低温、交变湿热和南海服役环境下的自然暴晒试验.结果表明,该膜层具有优良防护性能.
【Abstract】 The composite alumina film mix into nanometer silicon was prepared with nanometer silicon dissolved into electrolyte by means of electrochemistry approach. The composite film was investigated concerning of structure, composition, corrosion resistance mechanism by scanning electron microscope, X-ray analysis, electronic probetce. The protective performance of composite alumina film is optimum through tests such as salt fog, mildew, high temperature, low temperature, alternate wet heat, insolation etc.
【Key words】 composite alumina film； mix into nanometer silicon； corrosion resistance；
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅱ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TG174
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部