碳纳米管压阻效应及其应用研究
Piezoresistive effect and applications of carbon nanotube films
【Author】 WANG Wan-lu, LIAO Ke-jun, Lu Jian-wei, WAN Bu-yong, ZHANG Yi (Department of Applied Physics, Chongqing Uiversity, Chongqing 400044, China)
【机构】 重庆大学应用物理系；
【摘要】 利用了三点弯曲法研究了碳纳米管膜压阻效应.研究中所用的碳纳米管是用化学气相沉积法合成的.实验结果表明,碘掺杂和未掺杂的碳纳米管膜的压阻因子在500微形变和室温下分别为350和65,超过了单晶硅和多晶硅的压阻因子.同时还发现化学处理还能进一步增强碳纳米管膜的压阻效应.碘掺杂碳纳米管膜的压阻效应也许是由于在形变时带隙变化所致,而未掺杂碳纳米管压阻效应主要是由管之间接触电阻变化引起的.碳纳米管压阻效应可用于旋转速度的测量.
【Abstract】 The piezoresistive effect of Carbon nanotube films was investigated by a three point bending method, Carbon nanotubes in this study were synthesized by hot filament chemical Vapor deposition. The experimental results have shown that the gauge factors for I-dopted and undoped carbon nanotube films under 500 microstrain were about 350 and 65 respectively at room temperature, exceeding that of single-cystalline and polycrystalline silicon. It was also found that the piezoresistive effect in carbon nanotubes could be further enhanced by chemical treatment. The piezoresistive effect in carbon nanotubes may be caused by a strain-induced change in the band gap for the doped tubes and the intertube contact resistance and defects for the undoped tubes. This effect can be used in the measurements of rotational speed.
【Key words】 piezoresistive effect； carbon nanotubes； Ⅰ-doping； strain- induced change in resistance；
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅱ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TB383
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部