TiO2纳米线阵列生长机理的研究
Mechanism of formation of highly ordered TiO2 nanowire arrays
【Author】 ZUO Juan, SUN Lan, LAI Yue-kun, NIE Cha-geng, LIN Chang-jian(State Key Laboratory for Physical Chemistry of Solid Surface, Department of Chemistry,Xiamen University, Xiamen 361005, China)
【机构】 厦门大学化学系固体表面物理化学国家重点实验室；
【摘要】 采用两步氧化法制备了多孔氧化铝模板(AAO),并利用AAO结合用电化学诱导溶胶-凝胶法制备了锐钛矿型的TiO2纳米线阵列,探讨了形成TiO2纳米线阵列的生长机理.发现TiO2纳米线是由Au基底沿着孔洞逐步向上生长,直接生成纳米线,因而可以通过控制氧化铝模板的尺寸和电化学沉积的时间来控制纳米线的长径比.
【Abstract】 Highly ordered TiO2 nanowire arrays were prepared by an electrochemically induced sol-gel method. The mechanism of formation of the highly ordered TiO2 nanowire arrays with AAO templates was discussed. It is found that the TiO2 nanowires grow from the bottom along the wall of the AAO templates and thus it is possible to control the length and diameter ratio of TiO2 nanowires by controlling deposition time and AAO diameter.
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅱ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TB383
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部