节点文献
微乳液法制备纳米碱式硝酸铋
Micro-emulsion preparation of nanometer-sized basic bismuth nitrate stick
【Author】 FAN Li-ren, CAO Qi-gao, NI Tian-zeng, LI Hai-feng (Faculty of Material Science and Chemical Engineering, China University of Geosciences, Wuhan 430074, China)
【机构】 中国地质大学材料科学与化学工程学院；
【摘要】 本研究采用水溶液/Triton X-100/正己醇/环己烷反相微乳液体系,以硝酸铋为原料,氨水作沉淀剂,保持Triton X-100/环己烷/正己醇的体积比不变,改变所加入的水溶液体积和硝酸铋的浓度,得到了不同水核半径W0和不同硝酸铋浓度下的棒状纳米碱式硝酸铋.用TEM表征了不同条件下棒状产物的长度和直径.讨论了W0和硝酸铋浓度对棒状产物长度和直径的影响.
【Abstract】 Stick-like nanometer-sized basic bismuth nitrate that was confirmed by TEM and IR has been prepared successfully using aqua solution/TritonX-100/hexanol/ cyclohexane reversed phase micro-emulsion system. To fairly copy the stick structure of water-core, it is very important to optimize the experiment conditions especially keep volume ratio of Triton X-100/hexanol/cyclohexane and control water-core semi-diameter W0. With changing volume of water and concentration of bismuth nitrate, several size stick products have been obtained, their length and diameter were characterized by TEM.
【Key words】 nanometer-sized BiONO3 stick； micro-emulsion； preparation； morphology；
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅱ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TB383
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部