氧化铁纳米颗粒的合成、表征及特性研究
Synthesis, characterization and special property investigations of nanoFe2O3
【作者】 吕玉珍; 杨瑞枫; 梁芳; 赵子华; 齐兴义; 杨青林; 邓元; 嵇天浩; 郭林; 徐惠彬;
【Author】 Lu Yu-zhen, YANG Rui-feng, LIANG Fang, ZHAO Zi-hua, QI Xing-yi, YANG Qin-lin,DENG Yuan, JI Tian-hao, GUO Lin, XU Hui-bin (Institute of Material Science, Beijing University of Aeronautics and Astronautics, Beijing 100083, China)
【机构】 北京航空航天大学材料系;
【摘要】 采用水解法合成了聚乙烯吡咯烷酮(PVP)修饰的Fe2O3纳米材料(包括球形与纳米棒、球形与纳米线)和未经PVP修饰的菱形α-Fe2O3纳米材料.产物的紫外吸收边约为480nm,较体相材料明显“蓝移”.PVP修饰的纳米Fe2O3的矫顽力.饱和磁化强度和剩余磁化强度较未修饰的产物均有提高.
【Abstract】 Fe2O3 nanomaterials modified by PVP (including spherical nanoparticles and nanorods) and α-Fe2O3 rhombic nanoparticles without PVP were prepared using a hydrolysis method in this paper. The ultraviolet absorption edges of as-obtained products are about 480nm and shift to the short wavelength (blue shift) obviously compared with bulk material. The coercive force, saturation intensity and remanence of Fe2O3 nanomaterials modified by PVP are improved contrasted to Fe2O3 nanoparticles without PVP.
【Key words】 Fe2O3 nanomaterial; hydrolysis method; poly(N-vinyl-2-pyrrolidone)(PVP); macromolecule modify;
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅱ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TB383
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部