表面Ca2+交联对蒙脱石/聚丙烯酸（钠）吸水保水复合材料性能的影响
Influence of Ca2+ surface crosslinking on properties of montmorillonite/Polyacrylate superabsorbent composite
【Author】 XU Zhi-liang, FAN Li-ren, SHEN Shang-yue, XU Jian, LING Hui (The Faculty of Material Science and Chemical Engineering, China University of Geosciences, Wuhan 430074, China)
【机构】 中国地质大学(武汉)材料科学与化学工程学院；
【摘要】 采用水溶液聚合法制备了蒙脱石/聚丙烯酸(钠)吸水保水复合材料,并用CaCl2溶液对其进行表面交联处理.本文研究了表面交联剂CaCl2溶液的浓度和表面交联时间对复合材料吸水、保水性能以及凝胶强度的影响.实验结果表明,Ca2+表面交联处理提高了复合材料的保水能力和凝胶强度,同时也使其吸水能力略有下降.
【Abstract】 The research applied CaCl2 solution as surface crosslinking agent to Montmorillonite/Polyacrylate superabsorbent composite, and discussed effect of concentration of CaCl2 solution and surface cross-linking time on composite performances. The result shows that surface crosslinking improves water retention capability increases hydrogel strength, but reduced its water absorption capability a little.
【Key words】 superabsorbent； montmorillonite； surface crosslinking； water retention； hydrogel strength；
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅱ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TB332
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部