室温下海藻酸钙水凝胶与丙烯腈的快速接枝共聚
Quick graft copolymerization of acrylonitrile onto calcium alginate gel beads under ambient temperature
【Author】 XIAO Cong-ming, HE Yue-ying, LIN Xiao-dong (College of Materials Science and Engineering of Huaqiao University, Quanzhou 362011, China)
【机构】 华侨大学材料科学与工程学院；
【摘要】 探索了室温下、短时间内,海藻酸钙水凝胶与乙烯基单体丙烯腈接枝共聚的反应条件.在室温(20℃)下,5g平均直径为2.5mm的海藻酸钙水凝胶小球用8.5×10-2mol/L K2S2O8及7.0×10-2mol/LNaHSO3引发10min后,与浓度为6.22mol/L的丙烯腈反应30min,接枝率可达1520%.FTIR证实海藻酸钙水凝胶与丙烯腈之间发生了接枝共聚反应;而接枝共聚对水凝胶结构的影响,则用荧光测定法作了分析.
【Abstract】 The redox system was used to initiate the graft copolymerization of acrylonitrile onto calcium alginate gel beads (CAGB) under ambient temperature within short time. It was found that 5 grams CAGB could be initiated with 8.5×10-2mol/L K2S2O8and 7.0×10-2mol/L NaHSO3 for 10 min at 20"C, then reacted with 6.22mol/L acrylonitrile for another 30 min at the same temperature and the grafting percentage could be 1520%. FTIR spectra of CAGB and modifled CAGB extracted with dimethylformamide indicated that the graft copolymerization of acrylonitrile onto CAGB was carried out. The gel structure of CAGB and modified CAGB was analyzed vvith fluorimetry.
【Key words】 ambient temperature； calcium alginate gel beads； quick graft copolymerization； acrylonitrile；
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅱ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】O631
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部